| TiO2 content (%) | ≥ | 94 |
| Rutile ratio (%) | ≥ | 99.9 |
| CIE L | ≥ | 98.4 |
| b* | ≤ | 1.7 |
| CBU | ≥ | 14 |
| TCS | 100 | |
| Oil absorption (g/100g) | ≤ | 17 |
| Valatiles (105℃，%) | ≤ | 0.3 |
| Aqueous suspension pH | 6.5-8.5 | 8 |
| 45μm Sieve residue(%) | ≤ | 0.01 |
| Water solluble （%） | ≤ | 0.2 |
| Dispersibility by high-speed impeller mill (μm) | 15 | |
| D50 (μm) | 0.25 | |
| Surface treatment | Zr2O3, Al2O₃
organic treatment |
Architectural paints, automotive coatings, furniture lacquer, industrial coatings, inks, etc.
| GRADE | TYPE | COATING | PLASTIC | INK | PAPER MAKING | FIBER | |||||||
| Interior Architectural | Exterior Architectural | Industrial | Masterbatch | Engineering | Outdoor | Surface | Reverse Laminated | Surface Coating | Laminated | Polyester Filament Fiber | Staple Fiber | ||
| R-210 | Sulfate/Rutile | ● | ● | ● | O | O | O | O | O | ||||
| R-211 | Sulfate/Rutile | ● | ● | ● | |||||||||
| R-316 | Sulfate/Rutile | ● | ● | ● | O | O | |||||||
| R-317 | Sulfate/Rutile | ● | ● | ||||||||||
| R-318 | Sulfate/Rutile | ● | ● | ● | |||||||||
| R-319 | Sulfate/Rutile | ● | ● | ||||||||||
| CP-700 | Sulfate/Anatase | ● | ● | ||||||||||
| CP-600 | Sulfate/Anatase | ● | ● | ||||||||||
| CP-100 | Sulfate/Anatase | ● | ● | ● | ● | O | |||||||
| CR-3100 | Chloride | ● | ● | ● | ● | ||||||||
| CR-3101 | Chloride | ● | ● | ● | |||||||||
Note: “●” means highly recommended, “O” means recommended.